Study on preparation of superfine slag powder and modification of FGD gypsum
RONG Tianren1，BAO Xinhua1，ZHANG Jin2，YU Guoxin3
（1.Shanghai University，Shanghai 200444，China；2.Shanghai Yupei Special Building Material Company，Shanghai 201804，China；
3.Shanghai Haili Building Material Company，Shanghai 201906，China）
Abstract：Superfine slag powder with specific surface area>600 m2/kg was produced by removing the metallic iron efficiently
through using the pre-grinding and final-grinding system. Taking the superfine powder as the modifiers，then mixed them with
desulfurization gypsum and getting related index by testing. The results show，the superfine slag powder can efficiently improve the
properties of desulfurization gypsum. The optimum content of superfine slag powder was 15%，meanwhile compared to that without
the superfine slag powder，the water absorption of gypsum reduced by 5.8%，the flexural strength （7 d and 28 d） decrease by 9.6%
and 9.0%，respectively. While the compressive strength（7 d and 28 d） increase by 17.2% and 23.9%，respectively.
Key words：superfine slag powder，desulfurization gypsum，modifier
Study on preparation of superfine slag powder and modification of FGD gypsum
RONG Tianren1，BAO Xinhua1，ZHANG Jin2，YU Guoxin3
（1.Shanghai University，Shanghai 200444，China；2.Shanghai Yupei Special Building Material Company，Shanghai 201804，China；
3.Shanghai Haili Building Material Company，Shanghai 201906，China）
Abstract：Superfine slag powder with specific surface area>600 m2/kg was produced by removing the metallic iron efficiently
through using the pre-grinding and final-grinding system. Taking the superfine powder as the modifiers，then mixed them with
desulfurization gypsum and getting related index by testing. The results show，the superfine slag powder can efficiently improve the
properties of desulfurization gypsum. The optimum content of superfine slag powder was 15%，meanwhile compared to that without
the superfine slag powder，the water absorption of gypsum reduced by 5.8%，the flexural strength （7 d and 28 d） decrease by 9.6%
and 9.0%，respectively. While the compressive strength（7 d and 28 d） increase by 17.2% and 23.9%，respectively.
Key words：superfine slag powder，desulfurization gypsum，modifier