我碰到普硅水泥与硫铝酸盐水泥的拼混好像有问题,不知是否是普遍还是个例啊。
 

凯旋

论坛义工
管理成员
版主
注册
2006-09-29
帖子
16,029
反馈
5,510
QQ
88418669
是的,要特别注意比例的,有一篇文章,可供参考

掺硫铝酸盐水泥熟料的富硅酸盐水泥体系的性能研究
摘要:研究了硫铝酸盐水泥熟料对复合硅酸盐水泥性能的影响。研究表明,当复合水泥中掺入少量硫铝酸盐水泥熟料后.再配以适量的石膏,可以提高其早期强度,且随着硫铝酸盐水泥熟料掺量的增加,其凝结时间明显缩短。运用XRD等测试方法探讨了硫铝酸盐水泥熟料改善复合水泥性能的机理。硫铝酸盐水泥熟料水化形成的钙矾石和铝胶,对硅酸盐水泥熟料矿物水化有促进作用,这是水泥凝结加快、强度增加的主要原因。
关键词:复合硅酸盐水泥;硫铝酸盐水泥熟料;性能;机理

Abstract:The effect of sulphoaluminate cement on the performance of Portland cement was studied.The early strength of Portland-based composite cement is increased by the addition of proper amount of sulphoaluminate cement and gypsum.Th e setting time of studied cement is reduced as the amount of additive increased.By means of XRD and other measurements,the mechanism of perform ance modification of this composite cement was studied.The AFt and aluminate gel form ed during hydation,mainly cause the strerIgh increasing and setting time
reducing.
Key words:composite Portland cement;sulphoaluminate cement clinker;perform ance;mechanism
 

附件


申明:内容来自用户上传,著作权归原作者所有。如涉及侵权请点击 联系我们,我们将及时处理!

凯旋

论坛义工
管理成员
版主
注册
2006-09-29
帖子
16,029
反馈
5,510
QQ
88418669
硅酸盐水泥一高铝水泥一无水石膏复合胶凝体系的实验研究
http://www.drymt.com/threads/13804/
 

drymortar

技术总监
注册
2006-10-30
帖子
498
反馈
312
博士论文 硅酸盐_硫铝酸盐复合体系水泥研究
http://www.drymt.com/threads/13805/
 

sxgdy

封禁用户
注册
2011-01-19
帖子
232
反馈
9
QQ
1293464405
普硅水泥和硫铝酸盐水泥混合后会很快凝固,要特别注意比例。
 

固瑞德

研发工程师
注册
2014-06-03
帖子
153
反馈
61
QQ
798630007
正常的琉璃酸盐水泥在灌浆料的三元体系里的最佳比重是多少?或者说,占有整个体系胶凝材料的百分比是多少呢?
 

sxgdy

封禁用户
注册
2011-01-19
帖子
232
反馈
9
QQ
1293464405
每个地区的水泥都不太一样,只有通过若干试验才能找到最佳比例。
 